| Lupoy resins are high performance engineering resins based on polycarbonate. A number of specific grades are available, including general grades, reinforced grades and flame retardant grades.
Advantages of Lupoy :
Applications :
|
|
| Selection Guide |
Chemical name: Polycarbonate (PC)
| Grade | TDS | Melt Index, g/10 min (1.2kg, 300°C) | Haze, % | Rockwell Hardness, R Scale | Melt Index, g/10 min (2.16kg, 190°C) | Density, g/cm^3 | Mold Shrinkage, in/in | Water Absorption at 24h. 23°C, % | Refractive Index, no | Light Transmitance, % | Deflection Temperature Under Load (DTUL) at 4 mm at 0.45 MPa annealed, °C | Deflection Temperature Under Load (DTUL) at 4 mm at 1.8 MPa annealed, °C | Vicat Softening Point 50°C/hr 50N Load, °C | Coefficient of Linear Thermal Expansion at -40 to 82 °C, mm/mm/°C | Tensile Yield Strength, MPa | Ultimate Tensile Strength, MPa | Elongation at Yield, % | Elongation at Break, % | Tensile Modulus, MPa | Flexural Strength, MPa | Notched Izod Impact at 23°C, J/m |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Lupoy ® PC 1201-22 |  | 22 | 0.7-1.5 | 118 | V-2 | 1.2 | 0.005-0.007 | 0.15 | 1.586 | 89 | 142 | 139 | 147 | 68 x 10^-6 | 60 | 66 | 6 | 120 | 2340 | 96 | 750 |